CTS CorporationCTS Corporation

Soldering procedure

Soldering electrical wires to the screen-printed silver electrode makes an excellent and time-stable connection. Occasionally there can, however, be problems with wetting the solder tin on the silver surface and soldering can therefore be difficult.

This phenomenon is mainly caused by a reaction between sulphuric molecules in the atmosphere with the silver surface and the following formation of a silver-sulphide layer on the surface of the part. The formation and height of this layer is influenced by several factors such as age, pH, humidity, etc. 

In order to avoid such problems completely at any time, it can therefore be considered as good practice to gently clean the external electrodes on the part before soldering. A glass brush or steel wool is very useful for this operation. 

We recommend using soldering temperatures between 250 and 325 °C. Silver is soluble in the solder tin, and if the solder time is too long the electrode will completely dissolve in the solder. In order to increase the possible solder time, we recommend using a solder tin with silver content of 2-4 %. Even if the possible solder time is increased with this type of tin, we still recommend that the solder time does not exceed 2-3 seconds, in order to minimize heat transfer to the piezoceramic product an thus avoid the risk of depolarization of the piezoceramic material.

Solder materials
Soldering material must contain Ag. Noliac recommend the following for standard as well as Ultra-high vacuum applications:

96SC Tin/Silver/Copper with multicore flux (Flux type Crystal 400).

Recommended process
The wire is pre-soldered.

The Ag-electrode surface is cleaned with a glass brush to remove oxidation layer.

Soldering iron temperature is approximately “285ºC”.

The electrode surface is pre-soldered as follows:

  • A small amount of soldering material is melted at the tip of the soldering iron.
  • The soldering iron is held at the electrode surface for approximately 1 second
  • More soldering material is applied to form a small circular soldering material spot.
  • The pre-soldered wire is placed on top of the circular soldering material spot and soldered together.
  • If necessary, more soldering material is applied.

A piezo partner - what do we mean by that

Request for quote

We give you a competitive advantage by using our extensive knowledge to customize and optimize your piezo products. Thus, we will be your long-term piezo partner. Send your request today.

First name *
Last name *
Company *
Industry *
Email *
Phone
Country *
City
Choose product
Description
Please enter the result of the equation:
7 + 8 =
Close
Request for quote

Search tool

Performance Dimensions
Value
Max operating voltage / V
Min
Min free stroke / µm
Min
Min estimated blocking force / N
Min
Min
Max
Length or outer diameter / mm
Min
Max
Width or inner diameter / mm
Min
Max
Max height / mm
Max
Product category
Choose here...
  • Plate actuators
  • Plate stacks
  • Ring actuators
  • Ring stacks
  • Plate benders
  • Ring benders
  • Shear plate actuators
  • Shear stacks
  • 2D actuators
  • High temperature stacks
  • Damage tolerant stacks
Material
Choose here...
  • NCE51
  • NCE51F
  • NCE46
  • NCE57
  • NCE40
  • NCE41
  • NCE53
  • NCE55
  • NCE56
  • NCE59
  • NCE80
  • NCE81
  • 0,00
  • AA
  • Material
  • Type
  • 0.00
Search Clear
Next

Search on Noliac